Abstract
Delamination resistance of composite laminates can be improved with through-thickness reinforcement such as Z-pinning. This paper characterises the bridging response of individual carbon fibre/BMI Z-pins in mixed mode delamination at high loading rate using a split Hopkinson bar system. The unstable failure process in quasi-static tests, was also captured with high sampling rate instruments to obtain the complete bridging response. The energy dissipation of the Z-pins were analysed, and it was found that the efficacy of Z-pinning in resisting delamination growth decreased with an increase in mixed mode ratio, with a transition from pull-out to pin rupture occurring. The Z-pin efficacy decreased with loading rate for all mode mix ratios, due to the changing in failure surface with loading rate and rate-dependent frictional sliding.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Composites Part A: Applied Science and Manufacturing
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.