Abstract
Understanding the strengthening and deformation mechanisms in refractory high-entropy alloys (HEAs), proposed as new high-temperature material, is required for improving their typically insufficient room-temperature ductility. Here, density-functional theory simulations and a continuum mechanics analysis were conducted to systematically investigate the competition between cleavage decohesion and dislocation emission from a crack tip in the body-centered cubic refractory HEAs HfNbTiZr, MoNbTaVW, MoNbTaW, MoNbTiV, and NbTiVZr. This crack-tip competition is evaluated for tensile loading and a totality of 15 crack configurations and slip systems. Our results predict that dislocation plasticity at the crack tip is generally unfavorable – although the competition is close for some crack orientations, suggesting intrinsic brittleness and low crack-tip fracture toughness in these five HEAs at zero temperature. Fluctuations in local alloy composition, investigated for HfNbTiZr, can locally reduce the resistance to dislocation emission for a slip system relative to the configuration average of that slip system, but do not change the dominant crack-tip response. In the case of single-crystal MoNbTaW, where an experimental, room-temperature fracture-toughness value is available for a crack on a {100} plane, theoretical and experimental results agree favorably. Factors that may limit the agreement are discussed. We survey the effect of material anisotropy on preferred crack tip orientations, which are found to be alloy specific. Mixed-mode loadings are found to shift the competition in favor of cleavage or dislocation nucleation, depending on crack configuration and amplified by the effect of material anisotropy on crack tip stresses.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.