The chemical vapor deposition (CVD) method was employed to fabricate a two-dimensional (2D) MoS2 nanosheet and the related characteristics were measured. By using a new crystal Tm:Ca(Gd,Lu)AlO4 as laser medium, a laser-diode (LD) pumped dual-loss-modulated Q-switched laser with AOM and a MoS2 nanosheet was first presented as far as we know. The minimum pulse duration of 82 ns and the maximum peak power of 589 W were obtained under the modulation rate of 3 kHz. In comparison with the singly Q-switched laser with AOM or MoS2, the dual-loss-modulated Q-switched laser could generate shorter pulse width and higher peak power. The maximum compression ratio of pulse duration was 9.85 and the highest enhancement factor of peak power was 123. The experimental results hit a conclusion that 2D MoS2 nanosheet is potential in pulse laser at ∼2 µm and dual-loss-modulated Q-switching operation can compress the pulse duration and improve the peak power.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.