Abstract
Abstract The effect of sub-zero treatments on dry sliding wear performance of Vanadis 6 tool steel was investigated by pin-ondisc tests against three counterpart types: alumina, 100Cr6 ball bearing steel, and CuSn6 bronze. The microstructure of the examined steel consists of tempered martensitic matrix with very small amounts of retained austenite, and three carbide types. Sub-zero treatments increase the carbides count. The hardness of the steel increases with increasing the austenitizing temperature but slightly decreases with the application of sub-zero treatments. Sub-zero treatments affect the wear performance of the Vanadis 6 steel when tempered at the secondary hardening peak as follows: almost no effect of this kind of treatment was detected when alumina was used as a counterpart but moderate amelioration was recorded when either 100Cr6 steel or CuSn6 bronze was used in the sliding couple. This behaviour is attributed to the combined effect of hardness variations and changes in population density of carbides, due to application of sub-zero treatment.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.