Abstract
This work aimed to evaluate the effects of contact stress and slip ratio on wear and rolling contact fatigue of ER9 wheel steel and R260 rail steel couple under unlubricated conditions using a dual disk test. It was demonstrated that as either contact stress or slip ratio increased, so did the wear rate and surface damage of both ER9 wheels and R260 rail rollers. The wear rate of the ER9 wheel steel containing proeutectoid ferrite and the smaller structure size of pearlite increased significantly when compared to the rail steel containing fully pearlite in each pair. After testing according to the conditions used in this work, the surface hardness of the pearlitic rail steel was higher than that of the ferrite-pearlite wheel steel. The average hardening ratio of ER9 wheel steel and R260 rail steel was 0.7 and 1.28, respectively. This was consistent with the subsurface deformation angle. With full pearlite in the microstructure of rail steel, the main wear mechanism was predominantly caused by fatigue cracking and peeling, with some adhesive wear. Whereas the most prominent mechanism of the ferrite-pearlite wheel steel was adhesive wear, which was followed by spalling and small fatigue cracks.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.