Abstract
Low temperature (750 °C) and high stress (800 MPa) creep curves of single crystal superalloy ERBO/1 tensile specimens loaded in the 〈001〉 direction show two creep rate minima. Strain rates decrease towards a first sharp local creep rate minimum at 0.1% strain (reached after 30 min). Then deformation rates increase and reach an intermediate maximum at 1% (reached after 1.5 h). Subsequently, strain rates decrease towards a global minimum at 5% (260 h), before tertiary creep (not considered in the present work) leads to final rupture. We combine high resolution miniature creep testing with diffraction contrast transmission electron microscopy and identify elementary processes which govern this double-minimum type of creep behavior. We provide new quantitative information on the evolution of microstructure during low temperature and high stress creep, focusing on γ-channel dislocation activity and stacking fault shear of the γ′-phase. We discuss our results in the light of previous work published in the literature and highlight areas in need of further work.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.