Abstract
In order to push the development of nanowire-based solar cells further using optimized nanowire diameter and pitch, a doping evaluation of the nanowire geometry is necessary. We report on a doping evaluation of n-type InP nanowires with diameters optimized for light absorption, grown by the use of metal–organic vapor phase epitaxy in particle-assisted growth mode using tetraethyltin (TESn) as the dopant precursor. The charge carrier concentration was evaluated using four-probe resistivity measurements and spatially resolved Hall measurements. In order to reach the highest possible nanowire doping level, we set the TESn molar fraction at a high constant value throughout growth and varied the trimethylindium (TMIn) molar fraction for different runs. Analysis shows that the charge carrier concentration in nanowires grown with the highest TMIn molar fraction (not leading to kinking nanowires) results in a low carrier concentration of approximately 1016 cm−3. By decreasing the molar fraction of TMIn, effectively increasing the IV/III ratio, the carrier concentration increases up to a level of about 1019 cm−3, where it seems to saturate. Axial carrier concentration gradients along the nanowires are found, which can be correlated to a combination of changes in the nanowire growth rate, measured in situ by optical reflectometry, and polytypism of the nanowires observed in transmission electron microscopy.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.