Abstract
Thin film CdS/CdTe solar cell structures have been investigated by spatially resolved cathodoluminescence (CL) spectroscopy. A postgrowth CdCl2 treatment of the CdTe layer was found to homogenize the distribution of acceptor-like defects or impurities leading to optimized p-type conversion of the polycrystalline CdTe. For values of the growth temperature (TG) of about 600 °C, the intermixed region between the CdS layer and CdTe grains is surprisingly thin. However, for TG as large as 630–650 °C, a gradual decrease of the CdTe band gap due to sulfur intermixing appears to be present up to 0.6 μm from the CdS/CdTe interface. The CL spectra of the CdS window layer exhibit two broad bands centered at 1.72 (red) and 2.04 eV (yellow). The yellow one is quenched by the CdCl2 treatment, indicating passivation or promoted outdiffusion of Cd interstitials.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.