Abstract
NMMO-based carbon black (CB) dispersion was prepared and its properties as well as its compatibility with lyocell spinning solution were further investigated. Modified lignosulfonate (SP) was verified to be the preeminent dispersant for the preparation of NMMO-based CB dispersion with mass ratio of SP to CB 20% and water to NMMO 13%. The compatibility of NMMO-based CB dispersion with lyocell spinning solution had close relation with dispersant structure and CB content. Mass ratio of CB to cellulose affects the mechanical properties, color strength and crystallinity of lyocell fiber. 0.5% CB increased the breaking strength and elongation of lyocell fiber, whiles breaking strength and elongation of the lyocell fiber were reduced slightly when 2.0% CB was used. The dope dyed fiber showed excellent rubbing and washing fastness as well as migration resistance to water, ethanol and acetone.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.