A matrix of nine experiments was conducted on aluminum alloy 2139 samples made by an electron beam directed energy deposition additive manufacturing process to characterize the effect of magnesium vaporization loss on microstructure and properties. The nine-sample matrix included three different magnesium levels deposited onto material at three different temperatures. The goal was to quantify the variability in the deposited material as a function of allowable magnesium content and the local temperature of the substrate or previous layer. The results show that temperature variations in the substrate up to 100 K have no significant effect on the amount of magnesium loss; however, relatively large variations in Mg content, up to a ±0.25 wt%, can significantly affect the microstructure and mechanical properties. This is due to a change in how the precipitate phase forms, which influences the mechanism by which the alloy is strengthened.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.