Abstract
Full-Heusler compounds have three crystal structures with a different order degree; the highly ordered L21, partially disordered B2, and completely disordered A2 structures. To reveal the effects of the order degree on thermoelectric (TE) properties of the full-Heusler compounds, Mn2VAl samples with varied L21 and B2 order degrees are prepared by changing preparation conditions, and their Seebeck coefficients and electrical conductivities are measured in a wide temperature range. As the B2 order degree becomes higher, the Seebeck coefficient increases, leading to the increase of the power factor (PF). The maximum PF is 2.84 × 10−4 Wm−1 K−2 at 767 K for the Mn2VAl sample with the highest B2 order degree. This study demonstrates that the TE properties of Mn2VAl can be enhanced by increasing the fraction of the B2 phase. A relation between the Seebeck coefficient and crystal structures is also discussed based on the calculation of the electronic density of states of Mn2VAl with the L21 and B2 structures.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.