Abstract
A new joining method, i.e. ultrasonic plus resistance spot welding, is developed for dissimilar metal joining of aluminum alloy (Al) to steel. In this method, a thin Al insert is first joined to a steel sheet using the solid-state ultrasonic spot welding (USW). Next, the Al insert side of the steel sheet is welded to an Al sheet by the standard resistance spot welding (RSW). The U + RSW method is used to join 1-mm-thick AA6061-T6 to 0.9-mm-thick AISI 1008 steel with 0.4-mm-thick AA6061-T6 as the insert. The final Al/steel weld shows a brazing feature with liquid aluminum wetting and spreading on the solid steel surface. At welding current of 16.5 kA, a less than 1.5-μm-thick layer of intermetallics is observed at the Al insert/steel interface, corresponding to a high joint strength of 3.2 kN and a nugget pull-out failure mode. The formation of such a thin layer of intermetallics is attributed to the metallurgical bond formed at Al to steel interface by USW, which in turn reduces the electrical resistance and temperature at this interface during subsequent RSW. The effect of USW and RSW parameters on the interfacial microstructure, nugget size, joint strength and failure mode is further investigated.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.