Zirconium (Zr) is used in modern aluminum alloys to form dispersoids that control grain structure. The interaction of these dispersoids with the alloying elements used to strengthen aluminum remains poorly understood. We have used high resolution imaging and composition analysis via electron microscopy to study the Zr-rich dispersoids in AA7010, a commercial Al-Zn-Mg-Cu alloy, addressing this knowledge gap.We show that the dispersoids are not of the ideal Al3Zr stoichiometry, and contain Zn up to approximately 15 at%. Copper also concentrates in the dispersoids up to approximately 6 at%. Atomistic simulation was used to predict the partitioning, demonstrating favourable substitution of Zn and Cu onto the Al sublattice in the dispersoid phase, consistent with the measurements. We have also observed larger, facetted dispersoids, which are not of a phase observed in the binary Al–Zr system. Instead, we have found a previously unreported dispersoid structure (tI10 Ni4Mo structure type), which we propose is stabilized by the presence of Zn.We have calculated the total loss in Zn and Cu due to partitioning into the dispersoids. We show this is too small to directly have a detrimental effect on age hardening, but may have a secondary effect in promoting heterogeneous nucleation for undesirable quench induced precipitation.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.