Abstract
The ternary carbide Ti3SIC2 fabricated by a reactive hot‐press route is investigated by transmission electron microscopy. The material consists mainly of large elongated grains with planar boundaries, and is characterized by a low defect density. Dislocations are observed in the grains and at grain boundaries. Perfect dislocations with b = 1/3<1120> lying in (0001) basal planes are present. These basal plane dislocations are mobile and multiply as a result of room‐temperature deformation. All of the stacking faults observed lie in the basal planes.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.