Abstract
The systematic change in the dislocation density and characteristics that develop under cold rolling as a simulated deformation was studied in order to examine the fundamental behavior of dislocations in terms of the dislocation substructure formation. In particular, the dislocation density was quantified by X-ray line profile analysis (XLPA), which is effective for quantifying the dislocation density and character; positron annihilation lifetime (PAL), which is sensitive to vacancy-type lattice defects; the Bailey–Hirsch equation from the hardness (Hv); and transmission electron microscopy (TEM). The strain dependency of the dislocation density analyzed by XLPA, PAL, TEM, and Hv showed a similar tendency with an increase in the dislocation. In particular, the dislocation density by XLPA had good agreement with the results of TEM at low strain levels and with PAL at high strain levels. As a result, a combination of these techniques successfully showed the behavior of the dislocation substructure.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.