Abstract
ABSTRACTThe aim of this work was to study the deformation behavior of an Armco iron after severe plastic deformation by equal channel angular pressing (ECAP). Particular attention was paid to predict the dislocation density by different approaches like the model proposed by Bergström. Experimental measures of dislocation density by different techniques are used in the discussion. Cylindrical samples of ARMCO iron (8mm of diameter, 60mm of length) were subjected to ECAP deformation using a die with an intersecting channel of Φ=90° and outer arc of curvature of ψ= 37° die. Samples were deformed for up to 16 ECAP passes following route Bc. The mechanical properties of the material were measured after each pass by tensile tests. The original grain size of the annealed iron (70 μm) was drastically reduced after ECAP reaching grain sizes close to 300nm after 16 passes.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.