Abstract
This paper investigated the directional migration behavior of the alloying elements in the rafting process of the single crystal superalloy DD6 with [001] orientation under 300 MPa at 1000 °C. The microstructure of the single crystal superalloy DD6 was acquired by SEM. The results indicate that the rafting direction of γ ' phase is nearly perpendicular to stress axis. The matrix channel running parallel to the stress axis gets wider, but it will fade away gradually in vertical direction. Statistical analysis of the alloy components by TEM reveals the directional migrations of the elements Al, Re and W in the single crystal superalloy DD6. The element Al spreads to the matrix channel which is parallel to the stress axis, while Re and W diffuse to the matrix channel which is perpendicular to the stress axis, and obviously concentrate in the crossing area of the above mentioned channels.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.