Abstract
Nano-semiconductor materials coupled with piezoelectric effect have received extensive attention due to their wide application in catalysis. In this work, few-layered MoSe2 nanosheets were grown vertically on TiO2 nanorods (TNr) to synthesize a direct Z-scheme heterojunction, exhibiting efficient piezocatalytic and piezo-photocatalytic performance. The MoSe2/TNr heterostructure exhibited superior piezoelectric degradation efficiency, successfully removing over 98% of RhB within 360 s under continuous magnetic stirring in dark. Compared with piezocatalysis, the piezo-photocatalytic system possessed higher degradation efficiency and cycle stability. Furthermore, a piezo-photoelectric synergistic effect of nanocomposites was observed by current outputs. Under stirring conditions, the current density of depleted MoSe2/TNr and MoSe2 nanosheets were respectively 6.3 μA/cm2 and 5.5 μA/cm2. When light and stirring were applied, the MoSe2/TNr current density increased twice to 13.2 μA/cm2, while the MoSe2 nanosheets didn’t exhibit improvement. Through the direct Z-scheme heterojunction of MoSe2/TNr, photoexcitation and piezoelectric polarization work together to effectively replenish carriers under light irradiation, and then rapidly separate free charges through piezopotential. This work broadens the application prospects of piezocatalysis and piezo-photocatalysis in renewable energy harvesting and water purification.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.