Abstract
In this work, direct wafer bonding of SiC-SiC was accomplished by surface activated bonding (SAB) method at room temperatrue. The bonding energy of ~1.4 J/m2 was obtained without orientation dependence, which is much weaker than bulk SiC strength. Correspondingly, the tensile strength of bonding interface is ~12.2 MPa. The bonding mechanisms were investigated through Monte Carlo simulation and interface analysis by transmission electron microscopy (TEM) and energy dispersive X-ray spectroscopy (EDX). The formation of amorphous SiC during surface activation may eliminate the affects of orientation on bonding. In addition, the possible Si preferentially sputtering during surface activation is assumed to be the reason why direct wafer bonding of SiC-SiC cannot reach bulk SiC strength. After a rapid thermal annealing at 1273 K for 180 s in Ar, the tensile strength of bonding interface could be improved to the values higher than 21.6 MPa.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.