Abstract
Two electrodes for anodic water oxidation made by direct synthesis of inorganic catalysts onto conductive carbon fibre sheets are evaluated. As catalysts two Co- and Sb-containing phases were tested, that is, Co3 Sb4 O6 F6 and the new compound CoSbO4 . The compounds express large differences in their morphology: CoSbO4 grows as thin needles whereas Co3 Sb4 O6 F6 grows as larger facetted crystals. Despite the smaller surface area the latter compound shows a better catalytic performance. When the compound Co3 Sb4 O6 F6 was used it gave a low increase of +0.028 mV h-1 at an overpotential of η=472 mV after 10 h and a stability of +0.48 mV h-1 at an overpotential of η=488 mV after 60 h. The leakages of Co and Sb were negligible and only <0.001 at % Co and approximately 0.02 at % Sb were detected in the electrolyte.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.