Direct Preparation and Patterning of Iron Oxide Nanoparticles via Microcontact Printing on Silicon Wafers for the Growth of Single-Walled Carbon Nanotubes

Abstract

Direct fabrication of uniform patterns of Fe2O3·xH2O nanoparticles on the SiOx/Si surface was achieved by microcontact printing (μCP). The as-prepared poly(dimethylsiloxane) (PDMS) stamps with a hydrophobic surface were used. The “ink” was an FeCl3·6H2O ethanol solution. Fe2O3·xH2O nanoparticles were formed on the stamps from the hydrolysis of FeCl3 during the ink drying process and were then directly deposited onto the SiOx/Si surface with μCP. The nanoparticles were transferred to the areas beneath the “raised” portions of the stamp at low ink concentration but populated at the areas beneath the “recessed” portions of the stamp at high ink concentration. The hydrophobic property of the stamp surface cooperated with the gravity of the particles in bringing on such an exchange of recession and repousse. The density and size of the formed nanoparticles could be tuned by varying the ink concentration. The patterned Fe2O3·xH2O nanoparticles were used as the catalysts for the growth of single-walled carbon na...