Abstract
In this research, a new application of friction stir processing (FSP) in producing surface composite on circular billets was introduced. Al/Cu composite was fabricated by FSP on the surface of a 1050 aluminium cylinder with the diameter of 60 mm. Then this cylinder with surface composite was extruded with the extrusion ratio of 1.7. Finally, microstructure and microhardness were investigated before and after the extrusion. H13 hot work steel was used as the material of the tool whose pin diameter and length were 6 mm and shoulder diameter was 18 mm. The rotation and traverse speed of the tool were 1000 rpm and 25 mm/min respectively. The microstructural investigations show that the thickness of the composite layer decreases and a uniform layer of the composite remains on the surface after the extrusion. Also the microhardness measurements demonstrated that the hardness of the composite layer was higher than the base metal and the microhardness of all zones increased after the extrusion.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.