Direct energy deposition of Cu–Nb functionally graded layers for dissimilar joining titanium alloys and steels

Abstract

The heterogeneous compounds of titanium and iron steel are of wide interest in additive manufacturing. To prevent the formation of brittle intermetallic compounds, a layer of Nb and Cu was used. The use of the Nb and Cu interlayer successfully prevents the mixing of Ti and Fe, thus avoiding the formation of FexTiy brittle phases. In the Ti–Nb–(Nb + Cu–10Al) transition interlayer, it was possible to achieve the interlayer without the formation of brittle phases. The static tensile strength of the Grade1/316 L compounds with Nb–(Nb + Cu–10Al) interlayer is 335.5 MPa, the compounds exhibit ductile–brittle fracture.