Direct Electroplating Ruthenium Precursor on the Surface Oxidized Nickel Foam for Efficient and Stable Bifunctional Alkaline Water Electrolysis.

Abstract

Water electrolysis to produce hydrogen (H2) using renewable energy is one of the most promising candidates for realizing carbon neutrality, but its reaction kinetics is hindered by sluggish anodic oxygen evolution reaction (OER). Ruthenium (Ru) in its high-valence state (oxide) provides one of the most active OER sites and is less costly, but thermodynamically unstable. The strong interaction between Ru nanoparticles (NPs) and nickel hydroxide (Ni(OH)2) is leveraged to directly form Ru-Ni(OH)2 on the surface of a porous nickel foam (NF) electrode via spontaneous galvanic replacement reaction. The formation of Ru─O─Ni bonds at the interface of the Ru NPs and Ni(OH)2 (Ru-Ni(OH)2) on the surface oxidized NF significantly enhance stability of the Ru-Ni(OH)2/NF electrode. In addition to OER, the catalyst is active enough for the hydrogen evolution reaction (HER). As a result, it is able to deliver overpotentials of 228 and 15mV to reach 10mA cm-2 for OER and HER, respectively. An industry-scale evaluation using Ru-Ni(OH)2/NF as both OER and HER electrodes demonstrates a high current density of 1500mA cm-2 (OER: 410mV; HER: 240mV), surpassing commercial RuO2 (OER: 600mV) and Pt/C based performance (HER: 265mV).