Abstract
Direct coagulation casting via controlled release of high valance counter ions (DCC-HVCI) has been reported in recent years. In this paper, concentrated yttria-stabilized zirconia (YSZ) suspensions were coagulated using DCC-HVCI method with magnesium citrate as coagulating agent assisted by pH shift in the presence of glycerol diacetate. The effect of ammonium polyacrylate (PAA-NH4) on the dispersibility of YSZ powder was investigated. The influence of concentrations of glycerol diacetate and magnesium citrate on pH and viscosities of YSZ suspensions was studied. The results indicate that concentrated YSZ suspensions can be coagulated by adding 2vol% glycerol diacetate and magnesium citrate above 0.5wt% at room temperature for 2–5h. The compressive strength of coagulated wet samples is above 2.0MPa. YSZ ceramics sintered at 1450°C show homogeneous microstructures with relative densities of 98.9–99.2%. Flexural strength of YSZ ceramics is 869±84MPa.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.