Abstract
BackgroundS-vacancies play an essential role in various MoS2-catalyzed processes. Knowing that the size and shape of the S-vacancies affect the catalytic properties, this work investigates the diffusion of S-vacancies along different directions and whether these diffusion processes lead to the formation of specific surface patterns on a defective MoS2 monolayer. MethodsA first-principles-based kinetic Monte Carlo model is used to study how the S-vacancies of a vacancy cluster, i.e., a region where all surface S atoms are removed, migrate when the diffusion of the S-vacancies is limited to the [100], [120] and [1¯2¯0] directions, respectively. Significant findingsAt up to 600 K, the diffusion processes transform a vacancy cluster into a pattern of single S-atoms surrounded by six S-vacancy sites. Breaking this pattern requires high-barrier diffusion steps, only accessible at high temperatures where defective MoS2 sublimates. We have further found that the diffusion along the considered directions is very different, with the diffusion along the [120] direction being the slowest. In general, when diffusion is confined to a specific direction, the transformation of the vacancy cluster is slower than in the case with no constraints. This finding may help stabilize vacancy clusters on a catalyst.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Journal of the Taiwan Institute of Chemical Engineers
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.