Abstract
The aim of the present study is to investigate the effect of diffusion-doped silver on some physical properties of Bi 1.8Pb 0.4Ca 2.2Sr 2Cu 3O x superconducting samples and to calculate the diffusion coefficient and the activation energy of silver. The present work consists of three parts: (a) optimization of annealing temperature, (b) the effect of Ag diffusion-doped on microstructure and superconducting properties of Bi(Pb)CaSrCuO, and (c) calculation of diffusion coefficient of silver. First, to investigate the optimum annealing temperature we prepared Bi 1.8Pb 0.4Ca 2.2Sr 2Cu 3O x ceramic superconductors annealed at 830, 835, 840, 845, and 850 °C using the solid state reaction method. The investigations consist of XRD, SEM, dc resistivity, and transport critical current density measurements. The highest T c and J c values were observed for the sample annealed at 840 °C for 48 h (B840). Large grain size, denser surface, and high volume fraction of the high- T c phase were obtained for the sample B840. The diffusion doping of Bi 1.8Pb 0.4Ca 2.2Sr 2Cu 3O x by silver increased the critical current density from 123 to 696 A/cm 2 and the transition critical temperature by about 3 K compared with the undoped sample. Ag-doping increased the amount of high- T c phase and improved the surface morphology. It also caused an increase of the lattice parameter c by an amount of 0.15%. The temperature dependence of the silver diffusion coefficient in the range 600–800 °C is described by D=2.9×10 −4exp(−1.05 eV/ k B T). Possible reasons for the observed improvement in the structural and superconducting properties of the samples due to silver diffusion are discussed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.