Abstract
In production of Bi2Te3-based thermoelectric modules, Bi2Te3 materials were coated with electroless nickel (EN), electroless palladium, and immersion gold multilayers to suppress unanticipated interfacial reactions between Bi2Te3 and Sn-based solder alloys. However, the coating elements reacted with the solder alloys to yield intermetallic compounds (IMCs) at the Bi2Te3/solder and solder/Cu electrode interfaces. Significant Cu content from the Cu electrodes contributed to the IMCs along with to the coating and Sn elements. In this study, the influence of IMC composition on bonding strength and the characteristics of the Bi2Te3-based material/Cu electrode interface was investigated. An EN layer was plated onto Cu electrodes to suppress Cu diffusion from the electrodes into the solder alloy. IMCs mainly consisted of Sn and Cu elements in the case of uncoated Cu electrodes. When Cu electrodes were coated by the EN layer, Ni and Sn content prevailed in IMC composition. Additionally, IMCs at both the Bi2Te3/solder and solder/Cu electrode interfaces with Cu or Pd were thicker than those without Cu or Pd. Meanwhile, the bonding strength of the Bi2Te3-based material/Cu electrode interface with the EN layer on the Cu electrodes was lower than that of the interfaces without the EN layer.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.