Abstract
Multilayer composites are effective to improve the toughness of Tungsten (W). To demonstrate the toughing mechanism, a series of W/Ti multilayer composites are prepared by diffusion bonding at different temperatures in a spark plasma sintering system. It shows that the mechanical properties of the composites vary with the change of bonding temperature, which is closely related with the microstructures developed at different bonding temperatures. The bending strength of the composites bonding at 1100 °C is highest, which reaches 1847 MPa. However, the composites bonding at 1200 °C has absorbed the highest fracture energy during three-point bending tests. The different microstructures developed at different bonding temperatures are mainly due to the different diffusion behaviors of W and Ti elements. The activation energy of W diffusion into Ti and Ti diffusion into W is 87.69 KJ/mol and 152.20 KJ/mol, respectively. And the diffusion coefficient of W into Ti is two orders of magnitude higher than that of Ti into W. Thus, β-Ti has formed in the Ti layer due to W diffusion into Ti. Although α-Ti is precipitated in the β-Ti, solid solution strengthening is the main strengthening mechanism in the Ti layer. The toughening mechanism of the W/Ti multilayer composites is mainly crack deflection, and the plastic deformation of the Ti layer. Meanwhile, the fracture modes of these composites are proposed.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.