Abstract

We report gas and liquid transport measurements through membranes that have 40% voids made of 14 nm pores. A reactive polylactide-polynorbornenylethylstyrene block polymer is used as a structural template in the polymerization of dicyclopentadiene during the membrane formation process. After the membrane is cast, the pore structure is formed by etching the polylactide component using dilute aqueous base. The pore structure is isotropic; therefore, there is no need for special alignment techniques. Knudsen diffusion experiments and water flow experiments show pores with a tortuosity of 1.81 and a size of 14 nm, a diameter consistent with nitrogen adsorption and small-angle X-ray scattering measurements. These membranes are effective for ultrafiltration, with molecular weight cutoffs (MWCO) consistent with theoretical predictions with no adjustable parameters. These MWCO's can be tuned by changing the size of the constituent blocks in the templating copolymer.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.