Abstract
The purpose of this study was to determine the transformation temperatures for the austenitic, martensitic, and rhombohedral (R) structure phases in representative as-received commercial nitinol (NiTi) orthodontic wire alloys, to reconcile discrepancies among recent publications. Specimens were examined by differential scanning calorimetry (DSC) over a temperature range from approximately −170° C to 100° C, with a scanning rate of 10° C per minute. Two different pathways, with the intermediate R structure either absent or present, were observed for the transformation from martensitic to austenitic NiTi, whereas the reverse transformation from austenitic to martensitic NiTi always included the R structure. The enthalpy (ΔH) for the transformation from martensite to austenite ranged from 0.3 to 35 calories per gram. The lowest ΔH value for the nonsuperelastic Nitinol wire is consistent with a largely work-hardened, stable, martensitic microstructure in this product. The DSC results indicate that the transformation processes are broadly similar in superelastic, body-temperature shape-memory, and nonsuperelastic NiTi wires. Differences in bending properties for the NiTi orthodontic wires at room temperature and 37° C are due to the relative proportions of the metallurgical phases in the microstructures. (Am J Orthod Dentofac Orthop 1996;109:589-97.)
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: American Journal of Orthodontics and Dentofacial Orthopedics
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.