Differential degradation rate and underlying mechanism of a collagen/chitosan complex in subcutis, spinal cord and brain tissues of rat.

Abstract

Degradation rate is an important index for evaluating biomaterials. The authors' aim was to determine whether the degradation rate of biomaterials is different in distinct tissues and to clarify the underlying mechanism of degradation. The collagen-chitosan (CG-CS) composite scaffolds were prepared using freeze-drying technology. The porosity, water absorption and swelling ratio of the scaffolds were tested in vitro. The scaffolds were implanted into the subcutis, spinal cord and brain tissues of SD rats, the rate of degradation was assessed by continuous monitoring of weight loss, the pathological changes of target areas were observed by histological staining, and matrix metalloproteinase 9 (MMP-9) and lysozyme were detected at the rapid stage of degradation of the scaffolds. Physical and chemical property testing confirmed that CG-CS composite scaffold components can meet the biological requirements of in vivo transplantation. The in vivo experimental results showed that the scaffolds were completely absorbed in the subcutis at 12 days, the scaffolds in the spinal cord and brain groups exhibited progressive mass loss starting from the 3rd week, and a substantial fraction of the scaffold was degraded at 12 weeks. HE staining found that compared with the spinal cord and brain groups, macrophages and capillaries appeared earlier in the subcutis group, and the number was significantly higher (P < 0.05). Western blot analysis showed that the MMP-9 and lysozyme levels in the subcutis were higher than those in the spinal cord and brain (P < 0.05). The results of in vivo experiments demonstrated that the CG-CS scaffold has good biocompatibility and biodegradability, while the rate of degradation was significantly different between the three tissues at the same time point. Macrophage behavior and vascularization in different parts of the body may result in control over the balance of degradation and reconstruction.