Abstract
X-ray photoemission spectroscopy measurements were executed to compare the nature of defects in SrBi2Ta2O9 (SBT) and Bi4Ti3O12 (BTO) films. In the SBT film, it was found that the oxygen ions at the metal–oxygen octahedra were much more stable than those at the Bi2O2 layers. On the other hand, for the BTO film, oxygen vacancies could be induced both at the titanium–oxygen octahedra and at the Bi2O2 layers. We suggested that the difference in stability of the metal–oxygen octahedra should be related to different fatigue behaviors of the SBT and the BTO films.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.