Dielectrics for GaN based MIS-diodes

Abstract

GaN MIS diodes were demonstrated utilizing AlN and Ga{sub 2}O{sub 3}(Gd{sub 2}O{sub 3}) as insulators. A 345 {angstrom} of AlN was grown on the MOCVD grown n-GaN in a MOMBE system using trimethylamine alane as Al precursor and nitrogen generated from a wavemat ECR N2 plasma. For the Ga{sub 2}O{sub 3}(Gd{sub 2}O{sub 3}) growth, a multi MBE chamber was used and a 195 {angstrom} oxide is E-beam evaporated from a single crystal source of Ga{sub 5}Gd{sub 3}O{sub 12}. The forward breakdown voltage of AlN and Ga{sub 2}O{sub 3}(Gd{sub 2}O{sub 3}) diodes are 5V and 6V, respectively, which are significantly improved from {approximately} 1.2 V of schottky contact. From the C-V measurements, both kinds of diodes showed good charge modulation from accumulation to depletion at different frequencies. The insulator GaN interface roughness and the thickness of the insulator were measured with x-ray reflectivity.