Dielectric relaxation and magnetodielectric response in DyMn0.5Cr0.5O3

Abstract

We investigate the structural, magnetic, and magnetodielectric properties of DyMn0.5Cr0.5O3. The sample can be indexed with an orthorhombic phase with B site disordered space group Pbnm. The valence state of both Mn and Cr ions are suggested to be +3 based on the results of x-ray photoelectron spectroscopy. Two thermally excited dielectric relaxation at temperatures TN2 < T< 300 K and large magnetodielectric effect (MDC = 20%–30%) due to the disordered arrangement of Mn3+/Cr3+ ions associated with electron hopping between them are observed. The absence of any noticeable magnetoresistance effect (MR < 0.5%) demonstrates that the observed magnetodielectric effect is an intrinsic behavior. These results suggest that DyMn0.5Cr0.5O3 is a magnetodielectric compound, whose dielectric properties are dependence of the applied magnetic field, which exhibits such effects near room temperature and holds great promise for future device applications.