Abstract
Single phase perovskite Ba(Sr 1/3Nb 2/3)O 3 ceramics was prepared using the columbite precursor method. X-ray diffraction (XRD) technique is used to verify the single phase formation. It stabilizes in hexagonal phase with lattice constants a=12.1243 Å and c=15.3747 Å. Impedance analysis shows distributed relaxation time. Single semicircular arc observed in complex impedance plot confirms that only semiconducting grains are contributing to the polarization. The scaling behavior of both Z″ and M″ infers that the dynamical processes are temperature independent. Comparison of the impedance and electrical modulus data shows that the bulk response has contributions from both localized, i.e. defect relaxation, and non-localized conduction, i.e. ionic or electronic conductivity. The ac conductivity of the ceramics at higher temperatures indicates NTCR (negative temperature coefficient of resistance) behavior like semiconductors. The ac conduction activation energies are estimated from Arrhenius plots and conduction is largely due to hopping process.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.