Abstract
The frequency dependent dielectric and AC conductivity properties of different concentrations of Pr3+ doped Sr0.5Ca0.5TiO3 ceramics were investigated for the frequency range 100Hz to 2MHz at different temperatures. The morphology of the prepared samples was analyzed by using Field-Emission Scanning Electron Microscope images. The value of dielectric constant and dielectric loss decreases with increase in the frequency of the applied signal in all the samples. Also, the value of dielectric constant and dielectric loss decreased with doping of different concentrations of Pr3+ ions. The conductivity of the samples obeys Jonscher's power-law and shows a decrease with increasing doping concentration of Pr3+ ions. The higher value of real and imaginary part of impedance at lower frequency indicates the space charge polarization of the material and its absence at higher frequencies was confirmed from the low value of impedance at higher frequency region. The Cole- Cole parameters of the samples were calculated and the semi-circle observed indicates a single relaxation process and can be modeled by an equivalent parallel RC circuit. At lower frequency region, the value of dielectric constant and dissipation factor increases with increase in the temperature. Also the value of conductivity increases with temperature at high frequency region, due to the enhanced mobility of charge carriers.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.