Dielectric properties of hafnium oxide film prepared by HiPIMS at different O2/Ar ratios and their influences on TFT performance

Abstract

High-k hafnium oxide (HfO2) film was prepared by high power impulse magnetron sputtering (HiPIMS). The influences of oxygen supply on the plasma state, film properties and TFT performance were investigated. The films are near-stoichiometric and preferentially (−1 1 1)-orientated. When the oxygen supply increased from 1% to 3%, the excitation/ionization rate of the plasma species increased, leading to higher crystallinity, higher density, and lower oxygen vacancy defect concentration of the film, therefore improving the dielectric properties of the film. When the oxygen supply further increased to 5%, the excitation/ionization rate decreased, thereby leading to lower crystallinity, lower density, and higher oxygen vacancy defect concentration of the film, therefore deteriorating the dielectric properties of the film. The film deposited at 3% oxygen supply exhibited the best dielectric properties with the highest k value of 24 and the highest breakdown-electric field (4.7 MV/cm), which should be attributed to the high crystallinity, high density and low oxygen vacancy defect concentration of the film. Finally, transparent thin film transistors (TFTs) with ITO gate electrode, HfO2 gate dielectric layer and indium-gallium-zinc oxide channel were fabricated on flexible colorless polyimide substrate at full room temperature by all HiPIMS process. The fixed positive charges and k value of HfO2 film have significant effects on the TFT performance. The best TFT exhibited good electrical performance, featuring a remarkably low subthreshold swing of 0.13 V/decade. It also exhibited fair stability against bending and gate bias stress.