Abstract
Precursor powder of CaCu3Ti4O12 is prepared by a simplified coprecipitation process, in which an optimum reaction condition with ammonium acetate is used as buffer solution and pH=3.0 is proved by X-ray diffraction and scanning electron microscope. The CaCu3Ti4O12 ceramics samples are prepared by sintering the calcined powder at different temperatures (1040℃-1100℃). It is found that higher sintering temperature of CaCu3Ti4O12 ceramics will lead to lager grain size, higher dielectric constant and lower dielectric loss. The dielectric loss of CaCu3Ti4O12 ceramics is suggested to be due to DC electric conductivity, low-frequency relaxation loss and high-frequency relaxation loss. The low-frequency and high-frequency relaxations are related to grain boundary and oxygen vacancy defects respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.