Abstract
Dielectric properties of (Ba0.5Sr0.5)TiO3 and (Ba0.75Sr0.25)TiO3 thin films have been investigated, focusing on the effects of film structure and Ba/Sr compositions on the dielectric properties. Dielectric constant of the films increased with increasing grain size and with improvement in film crystallinity. For the 50-nm-thick films deposited at 660° C, the dielectric constant of 400 for the (Ba0.5Sr0.5)TiO3 film is larger than that of 320 for the (Ba0.75Sr0.25)TiO3 film. This indicated that dielectric constant is affected by the ratio of Ba/Sr composition. Leakage current density of less than 1×10-7 A/cm2 at 1 V and SiO2 equivalent thickness of 0.38 nm are measured at 120° C for 660° C-deposited (Ba0.5Sr0.5)TiO3 film of 30 nm in thickness. The (Ba0.5Sr0.5)TiO3 film has the possibility for application to generations beyond 256 Mbit dynamic random access memories.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.