Abstract
The dielectric and microwave properties of ( x)BaZn 1/3Nb 2/3O 3–(1 − x)BaMg 1/3Nb 2/3O 3 (BMZN) mixture were investigated. The complex perovskite-type ceramics Ba(Zn 1/3Nb 2/3)O 3 (BZN) and Ba(Mg 1/3Nb 2/3)O 3 (BMN) have a high dielectric constant ( ɛ r = 39 and 33, respectively), but while BZN has a relative low firing temperature (∼1350 °C), BMN has a too high sintering temperature (>1500 °C) to make it attractive in some technological applications. Mixing these two dielectric ceramics in different proportions and adding some sintering agents (like glassy B 2O 3 and LiF) the sintering temperature can be decreased, and XRD patterns indicates the formation of a solid solution for all x values investigated. The dielectric properties are preserved or even improved for some specific combinations. For BMZN ( x = 1/4), without any dopants, the Q f factor is 76.7 THz for f = 7.6 GHz and the temperature coefficient of the resonant frequency τ f is −4 ppm/°C, which is the best value for BMZN. These values make BMZN compounds suitable for microwave resonator applications. We highlight in this paper that BMZN materials can be successfully sintered at low temperature (i.e. 940 °C), opening opportunities to manufacture base metal electrodes multilayer ceramic capacitors (BME-MLCC).
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.