Abstract
This study discusses aluminoborosilicate glasses with La2O3 and CeO2. Structural, thermal, and dielectric properties were investigated by FTIR, DSC, and impedance analyzer. Results indicate that more Q3 and Q4 would form at the sample with the same amount of La2O3 and CeO2, meaning the most compact structure, while more La2O3 would lead to a loosen network. Meanwhile, glasses obtained the best dielectric properties here, and the dips in dielectric constant and loss are ascribed to the structural changes in the glass network. The glass transition temperature, Tg ascends first and then declines, due to the variation of bond strength and non-bridge oxygen content, as well as changes in field strength. Parameters for thermal stability decrease firstly and then increase slightly, indicating small changes in thermal stability. The glass density gradually increases, which is mainly from the small field strength of La3+ ions and the larger molar mass of La2O3.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.