Abstract
. A doping CaO-B2O3-SiO2 system low temperature co-fired ceramics (LTCC) was prepared with a mixture of high temperature melting glass and sol-gel glass for different ratio. The effects of sol-gel glass content on the microstructure, crystalline phases, sintering properties and dielectric properties of CaO-B2O3-SiO2 system were investigated at 850°C. The results show that the samples with sol-gel glass doping had little change in phase composition, but contained more calcium silicates, and less calcium borate. As the amount of sol-gel glass increased, the shrinkage improved, the sintered density slightly decreased, the dielectric constant (εr) reduced, and the dielectric loss (tgδ) decreased. When the amount of sol-gel glass was 14.5wt%, εr and tgδ of the doping sample were 5.80, 4.6×10-5 (at 1 MHz), respectively. Moreover, the doping system had a good matching ability with gold slurry and Au-Pt-Pd slurry.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.