Abstract

Porous lead zirconate titanate–lead cobalt niobate 0.8Pb(Zr1/2Ti1/2)O3–0.2Pb(Co1/3Nb2/3)O3 (PZT–PCN) piezoelectric ceramics were fabricated by introducing pore-forming agent polymethyl methacrylate (PMMA), and the effect of sintering behavior on their microstructure, dielectric, and piezoelectric properties were investigated. The optimum sintering procedure was designed according to the thermogravimetric analysis of pore former. Finally the electrical properties were measured.The porosity of PZT–PCN ceramics decreased and the grain size increased with an increase in the sintering temperature at a fixed PMMA addition.“An increase in density with sintering temperature from 1050 to 1250°C results into an increase in longitudinal piezoelectric coefficient (d33) and relative dielectric constant (εr). This ‘in turn’ enhanced the hydrostatic figure of merit (dhgh) of the ceramics material”.The hydrostatic figure of merit (dhgh) of 24% porous PZT–PCN ceramics was eleven times more than that of dense ceramic. This kind of porous ceramic could be a promising candidate for medical diagnostic devices.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.