Abstract
The dielectric, piezoelectric and physical properties of the [001]-oriented rectangular plate and beam mode of Pb[(Mg1/3Nb2/3)0.52(Yb1/2Nb1/2)0.15Ti0.33]O3 (PMN-PYbN-PT) ternary single crystals (SC) poled by alternate current poling (ACP) were investigated. The dielectric permittivity and average piezoelectric coefficient d33 were 6800 and 2490 pC/N, respectively, for the rectangular plate sample after ACP, which were 31% and 41% larger than those of the same sample after conventional direct current poling. The highest value of d33 reached 2750 pC N−1. The dielectric loss was reduced by 31%; nevertheless, the d33 improved after ACP. The beam mode electromechanical coupling factor () was 91% by using ACP, showing the highest value among all relaxor-PT SC systems reported so far. The regular periodic stripe domains were observed in ACP samples, showing high domain wall density and uniform domain size. This work demonstrates that the high performance after ACP is an effective method of improving the relaxor-PT SC transducers.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.