Abstract
In this study, 0.97(Na0.52K0.443Li0.037)(Nb0.96-xSb0.04Tax)O3–0.03(Bi0.5Na0.5)0.9(Sr)0.1ZrO3 ceramics were fabricated as a function of Ta substitution by conventional solid state method in order to develop the excellent composition ceramics for piezoelectric actuator, and their dielectric and piezoelectric properties were investigated. As the chemical composition results of 0.97(Na0.52K0.443Li0.037)(Nb0.96-xSb0.04Tax)O3–0.03(Bi0.5Na0.5)0.9(Sr)0.1ZrO3 system, we obtained the following results: When Ta was substituted for the ceramics, all the ceramics possessed a perovskite structure. When the substitution of Ta was 0, 0.01 and 0.02, Morphotropic phase boundary (MPB) region, which is coexist with rhombodedral phase and tetragonal phase was appeared. With further increasing the Ta substitution, the ceramics showed the strengthened tetragonal phase together with the coexistence of rhombodedral phase and tetragonal phase. The NKN-BNZ ceramics with x = 0.02 showed excellent piezoelectric properties. The density (ρ), piezoelectric constant (d33), planar piezoelectric coupling coefficient (kp), mechanical quality factor (Qm), and dielectric constant (er) were optimized as 4.456 (g/cm3), 269 (pC/N), 0.419, 51, 1644, respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Transactions on Electrical and Electronic Materials
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.