Dielectric and phonon spectroscopy of Nb-doped Pb(Zr1-yTiy)O3-CoFe2O4 composites

Abstract

Broad-band dielectric and phonon response of Nb-doped (1-x)Pb(Zr1-yTiy)O3-xCoFe2O4 composites with x = 10%–30% was investigated between 0.1 MHz and 100 THz. At room temperature, a broad distribution of relaxation times causes a constant dielectric loss below 1 GHz. Above room temperature, a strong Maxwell-Wagner relaxation process dominates below 1 GHz due to the conductivity of CoFe2O4 (CF). Two additional relaxation processes are seen between 1 GHz and 1 THz. The lower-frequency one, coming from domain wall motion, disappears above TC ≈ 650 K. The higher-frequency component slows down on heating towards TC, because it is the central mode, which drives the ferroelectric phase transition. Time-domain THz transmission and infrared reflectivity spectra reveal a mixture of polar phonons from both ferroelectric Nb-doped Pb(Zr,Ti)O3 (PZTN) and magnetic CoFe2O4 (CF) components, while the micro-Raman scattering spectra allow to study phonons from both components separately. Similar temperature behavior of phonons as in the pure PZTN and CF was observed. While in CoFe2O4 the Raman-active phonons gradually reduce their intensities on heating due to increasing conductivity and related reduced Raman-scattering volume, some phonons in PZTN disappear above TC due to change of selection rules in the paraelectric phase. Like in the pure Pb(Zr,Ti)O3, the soft phonon and central modes were also observed.