Abstract
The 0.5(BiGd0.05Fe0.95O3)-0.5(PbZrO3) composite was synthesized by means of a high temperature solid-state reaction technique using high purity ingredients. Preliminary X-ray structural analysis confirms the formation of the composite. The dielectric constant and loss tangent have been studied. The impedance parameters have been measured using an impedance analyzer in a wide range of frequency (102–106 Hz) at different temperatures. The Nyquist plot suggests the contribution of bulk effect only and the bulk resistance decreases with a rise in temperature. Electrical impedance confirms the presence of grain effect and hopping mechanism in the electrical transport of the material. The dc conductivity increases with a rise of temperature. The frequency variation of ac conductivity shows that the compound obeys Jonscher’s universal power law and from Jonscher’s power law fit confirms the Small Polaron (SP) tunneling effect. Temperature dependence of dc and ac conductivity indicates that electrical conduction in the material is a thermally activated process.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.