Abstract
Sputter-deposited amorphous diamond-like carbon (DLC, a-C) on silicon has been investigated with respect to micro electro mechanical systems (MEMS) applications. Sputtered a-C with a content of diamond-like sp3 bonded carbon of around 25% showed a high hardness of up to 30 GPa. Self-supporting cantilevers of 0.5 µm in thickness, several hundreds of µm in length and some tens of µm in width have been successfully realized using lift-off patterning of DLC and anisotropic silicon etching. The mechanical properties of DLC (Young's modulus, stress, stress gradient fracture strength) were characterized by cantilever deflection analyses. DLC strain gauge resistors integrated on micromachined silicon boss membranes were investigated under tensile and compressive loading. Piezoresistive gauge factors in the range of 20–30 were observed at temperatures between room temperature and 50 °C.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.