Abstract
Lead borate glasses containing 30 to 60 mol% PbO were prepared by melt quenching technique and devitrified by long duration heat treament in the supercooled region. Glasses crystallized on heating above their glass transition temperature, and the crystalline phases produced on devitrification were characterized by XRD and DSC analyses. Glass with 30 mol% PbO slowly formed a solid solution of Pb6B10O21 and Pb5B8O17 crystalline phases, while glasses with 40 and 50 mol% PbO formed a mixture of Pb6B10O21, Pb5B8O17 and the remanent glassy phase. Glasses with higher PbO concentration of 56 to 60 mol% devitrified completely and produced only Pb5B8O17 crystalline phase. Lead borate glasses with PbO concentration of 40 to 50 mol% showed maximum thermal stability against devitrification, the ease of crystallization of glasses was correlated with the fraction of tetrahedral borons in them.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call